The production of chitosan nanofiber mats by electrospinning presents serious difficulties due to the lack
of suitable solvents and the strong influence of processing parameters on the fiber properties. Two are
the main ...
Panadero, Juan Alberto; Vikingsson, Line Karina Alva; Gómez Ribelles, José Luís; Sencadas, Vitor Joao Gomes Da Silva; Lanceros-Mendez, Senentxu(Elsevier, 2013-12)
Tissue engineering applications rely on scaffolds that during its service life, either for in-vivo or in vitro applications, are under loading. The variation of the mechanical condition of the scaffold is strongly relevant ...
Ribeiro, Clarisse; Panadero Pérez, Juan Alberto; Sencadas, Vitor Joao Gomes Da Silva; Lanceros Mendez, Senen; Tamaño Machiavello, María Noel; Moratal Pérez, David; Salmerón Sánchez, Manuel; Gómez Ribelles, José Luís(IOP Publishing: Hybrid Open Access, 2012)
Due to the large potential of electroactive materials in novel tissue engineering strategies, the aim of this work is to determine if the crystalline phase and/or the surface electrical charge of electroactive poly(vinylidene ...
Sencadas, Vitor Joao Gomes Da Silva; Pitaes, Alexandre; Benelmekki, Maria; Gómez Ribelles, José Luís; Lanceros Mendez, Senen(American Chemical Society, 2011)
[EN] This work reports on the nucleation of the beta-phase of poly(vinylidene fluoride) (PVDF) by incorporating CoFe2O4 and NiFe2O4 nanoparticles, leading in this way to the preparation of magnetoelectric composites. The ...
Correia, Daniela M.; Ribeiro, Clarisse; Sencadas, Vitor Joao Gomes Da Silva; Botelho, G.; Carabineiro, S.A.C.; Gómez Ribelles, José Luís; Lanceros-Mendez, Senentxu(Elsevier, 2015-08)
Electrospun poly(vinylidene fluoride) (PVDF) fiber mats find applications in an increasing number of areas, such as battery separators, filtration and detection membranes, due to their excellent properties. However, there ...
Chitosan fiber mats were successfully processed by electrospinning. The as-spun fiber mats were neutralized with ethanol and cross-linked with glutaraldehyde. A decrease of the fiber average diameter from 243 +/- 43 nm ...
Ribeiro, Clarisse; Sencadas, Vitor Joao Gomes Da Silva; Miguel Costa, Carlos; Gómez Ribelles, José Luís; Lanceros-Mendez, Senentxu(National Institute for Materials Science, 2011)
[EN] Biodegradable poly(L-lactic acid) (PLLA) microfibers were prepared by electrospinning by varying the applied potential, solution flow rate and collector conditions. PLLA fibers with smoothly oriented and random ...
[EN] Poly(lactic acid) (PLA) electrospun membranes were obtained by electrospinning and
characterized by scanning electron microscopy (SEM) and thermal analysis. The polymer
membranes showed a random fiber distribution ...