Garcia, T.; Lopez, J. M.; López Nieto, José Manuel; Sanchis, R.; Dejoz, A.; Vazquez, M. I.; Solsona, B.(Elsevier, 2015-06)
[EN] H-2 and propylene can be obtained from propane and oxygen in defect using appropriate catalysts. Meanwhile propylene is formed from propane via oxidative or non-oxidative dehydrogenation, molecular hydrogen can be ...
Solsona Espriu, Benjamin Eduardo; Concepción Heydorn, Patricia; López Nieto, José Manuel; Dejoz, A.; Cecilia, J. A.; Agouram, S.; Soriano Rodríguez, Mª Dolores; Torres, V.; Jimenez-Jimenez, J.; Rodriguez Castellon, E.(Royal Society of Chemistry, 2016)
[EN] Porous clay heterostructures (PCH) have shown to be highly efficient supports for nickel oxide in the oxidative dehydrogenation of ethane. Thus NiO supported on silica with a PCH structure shows productivity towards ...
Solsona Espriu, Benjamin Eduardo; López Nieto, José Manuel; Concepción Heydorn, Patricia; Dejoz, A.; Ivars Barceló, Francisco; Vazquez, M. I.(Elsevier, 2011-05-16)
Ni-W-O mixed oxides were prepared through the evaporation of aqueous solutions of nickel nitrate and ammonium tungstate and calcined in air at 500 degrees C for 2 h. The catalysts were characterized by several techniques ...
[EN] The robustness of one selected Ni-W-O catalyst has been studied in the oxidative dehydrogenation of ethane. This catalyst initially deactivates for the first 10 h online decreasing 15% of its catalytic activity compared ...
López Nieto, José Manuel; Solsona Espriu, Benjamin Eduardo; Concepción Heydorn, Patricia; Ivars Barceló, Francisco; Dejoz, A.; Vazquez, M. I.(Elsevier, 2010-11-17)
[EN] The catalytic properties of MoVTeNbO catalysts during the selective oxidation of short chain alkanes and olefins (C-2-C-4) have been comparatively studied The main reaction products have been ethylene from ethane ...
Botella Asuncion, Pablo; Dejoz, A.; Abello, M. C.; Vazquez, M. I.; Arrua, L.; López Nieto, José Manuel(Elsevier, 2009-04-30)
[EN] Mo-V-X (X = Nb, Sb and/or Te) mixed oxides have been prepared by hydrothermal synthesis and heat-treated in N(2) at 450 degrees C or 600 degrees C for 2 h. The calcination temperature and the presence or absence of ...