Sánchez Tovar, Rita; Montañés Sanjuan, María Teresa; García Antón, José; Guenbour, A.; Ben Bachir, A.(Elsevier, 2011-04)
[EN] This paper studies the general corrosion behaviour of the micro-plasma arc welded AISI 316L stainless steel in phosphoric acid at different temperatures (25-60°C) and at a Reynolds number of 1456. Galvanic corrosion ...
Escrivá Cerdán, Clara; Blasco Tamarit, María Encarnación; García García, Dionisio Miguel; García Antón, José; Guenbour, A.(Elsevier, 2012-10-01)
The electrochemical behaviour of the highly alloyed austenitic stainless steel UNS N08031 (Alloy 31) in a contaminated phosphoric acid solution is studied using potentiodynamic curves, EIS and Mott–Shottky. The relative ...
[EN] Galvanic corrosion of non-welded/welded AISI 316L SS at different temperatures (25 degrees C to 60 degrees C) at a Reynolds number of 1456 in phosphoric acid has been studied using polarization curves (by the mixed ...
[EN] The objective of this work is to study the effect of welding on the corrosion resistance of the austenitic stainless steel Alloy 59 (UNS N06027) as well as the galvanic corrosion generated by the base/weld pair estimated ...
[EN] In this work, the galvanic corrosion of the base AISI 316L stainless steel/micro-plasma arc welded AISI 316L stainless steel in phosphoric acid solutions polluted with sulphuric acid and chlorides was studied by means ...
Escrivá Cerdán, Clara; Blasco Tamarit, María Encarnación; García García, Dionisio Miguel; García Antón, José; Guenbour, A.(Elsevier, 2012-03)
The influence of temperature (20–80 °C) and chloride concentration (0.06–0.42 wt.% KCl) on the electrochemical behaviour of the UNS N08031 was studied in 40 wt.% polluted phosphoric acid solution.
Passivation behaviour ...