LZS/Al2O3 nanostructured composites obtained by colloidal processing and spark plasma sintering

Abstract

[EN] Li2O-SiO2-ZrO2 (LZS) glass-ceramics have high mechanical strength, hardness, resistance to abrasion and chemical attack, but also a high coefficient of thermal expansion (CTE), which can be reduced adding alumina nanoparticles. The conventional glass-ceramic production is relatively complex and energy consuming, since it requires the melting of the raw materials to form a glass frit and a two-step milling process to obtain particle sizes adequate for compaction. This study describes the preparation of LZS glass-ceramics through a colloidal processing approach from mixtures of SiO2 and ZrO2 nanopowders and a Li precursor (lithium acetate obtained by reaction of the carbonate with acetic acid). Concentrated suspensions were freeze-dried to obtain homogeneous mixtures of powders that were pressed (100 MPa) and sintered conventionally and by spark plasma sintering. The effect of the alumina nanoparticles additions on suspensions rheology, sintering behavior and properties such as thermal expansion, thermal conductivity, hardness and Young's modulus were evaluated. (C) 2017 Elsevier Ltd. All rights reserved.