Influence of different technological-environmental parameters on the evolution of resistance of concrete, produced in the province of Valencia

Abstract

[EN] In this article on the basis of analysis of the influence of different technological-environmental parameters, such as the type of cement, water/cement ratio, initial curing temperature, time of conservation work, content of cement, additions, additives and consistency in the evolution of the concrete compressive strength, obtained a calculation equations and some graphs to estimate the resistance evolution of the concrete HA-25/B/20/IIa and HA-30/B/20/IIa from 3 to 28 days for each initial temperature curing interval specified and for the sample of concrete. So are based on 67782 data of different compressive strength of prepared concrete in the province of Valencia during the years 1996 to 2011, that has allowed to compare the equations obtained from regression with a significant database.

[ES] En este artículo partiendo del análisis de la influencia de diferentes parámetros tecnológico-ambientales, como son el tipo de cemento, relación agua/cemento, temperatura inicial de curado, tiempo de conservación en obra, contenido de cemento, adiciones, aditivos y consistencia en la evolución de la resistencia a compresión del hormigón, se obtienen unas ecuaciones de cálculo y unas gráficas que estiman la evolución de la resistencia de los hormigones HA-25/B/20/IIa y HA-30/B/20/IIa de 3 a 28 días para cada intervalo de temperatura inicial de curado especificado y para toda la muestra de hormigón. Para ello se parte de 67.782 datos de resistencia a compresión de diferentes hormigones preparados de obra en la Provincia de Valencia durante los años 1996 a 2011, que ha permitido contrastar las ecuaciones obtenidas de la regresión contrastar las ecuaciones obtenidas de la regresión con una base de datos significativa.