Espinosa, L.; Bonache Bezares, V.; Salvador Moya, MD. (2011). Friction and wear behaviour of WC-Co-Cr3C2-VC cemented carbides obtained from nanocrystalline mixtures. Wear. 272(1):62-68. doi:10.1016/j.wear.2011.07.012
Por favor, use este identificador para citar o enlazar este ítem: http://hdl.handle.net/10251/79773
Title:
|
Friction and wear behaviour of WC-Co-Cr3C2-VC cemented carbides obtained from nanocrystalline mixtures
|
Author:
|
Espinosa, L.
Bonache Bezares, Victoria
Salvador Moya, Mª Dolores
|
UPV Unit:
|
Universitat Politècnica de València. Instituto de Tecnología de Materiales - Institut de Tecnologia de Materials
Universitat Politècnica de València. Escuela Técnica Superior de Ingenieros Industriales - Escola Tècnica Superior d'Enginyers Industrials
|
Issued date:
|
|
Abstract:
|
The effect of adding Cr3C2, VC or a mixture of both as a grain growth inhibitors to cemented carbides obtained from WC-12 wt.%Co nanocrystalline mixtures on the behaviour of friction and dry sliding wear have been studied. ...[+]
The effect of adding Cr3C2, VC or a mixture of both as a grain growth inhibitors to cemented carbides obtained from WC-12 wt.%Co nanocrystalline mixtures on the behaviour of friction and dry sliding wear have been studied. All the wear tests were performed on a tribometer with ball on disc configuration, using a WC-6 wt.%Co ball as a counterpart with normal contact loads of 40 and 60 N, sliding distance of 2000 m and a sliding speed of 0.1 m/s. A significant reduction in the wear rates was observed by the effect of the aforementioned additives, in particular for the VC, which showed an increase in the wear resistance of the order of 90%. The analysis of wear and surface damage were correlated to the observed behaviour.
[-]
|
Subjects:
|
WC-Co nanocrystalline
,
Grain growth inhibitor
,
Dry sliding wear
,
Wear resistance
|
Copyrigths:
|
Cerrado |
Source:
|
Wear. (issn:
0043-1648
) (eissn:
1873-2577
)
|
DOI:
|
10.1016/j.wear.2011.07.012
|
Publisher:
|
Elsevier
|
Publisher version:
|
http://dx.doi. org/10.1016/j.wear.2011.07.012
|
Project ID:
|
Ministry of Education and Science
MAT2006-12945-C03-02
MAT2009-14144-C03-02
|
Thanks:
|
The authors would like to thank the Ministry of Education and Science, and the support received through the Projects MAT2006-12945-C03-02 and MAT2009-14144-C03-02, as well as the AECI for the realization of the doctoral ...[+]
The authors would like to thank the Ministry of Education and Science, and the support received through the Projects MAT2006-12945-C03-02 and MAT2009-14144-C03-02, as well as the AECI for the realization of the doctoral thesis by L. Espinosa in the ITM of the UPV.
[-]
|
Type:
|
Artículo
|