Optimum use of sugar cane straw ash (SCSA) in alkali-activated binders based on blast furnace slag (BFS)

Abstract

[EN] Alkali-activated binders (AABs) are a material obtained from the combination of a solid precursor and an alkaline activating solution. In this study, one solid precursor used was blast-furnace slag (BFS) and the other was an agro waste: sugar cane straw ash (SCSA). Sodium hydroxide was used for preparing activating solutions. In order to reach the potential reactivity of the SCSA, a study varying the BFS/SCSA mass ratio and H2O=Na2O molar ratio was carried out. The BFS/SCSA ratio varied from 100=0 to 70=30, and H2O=Na2O was studied in the range of 11.1¿18.5. To fulfill this objective, specimens were assessed by their compressive strength of mortars and microstructural studies of pastes [X-ray diffraction (XRD); thermogravimetric analysis (TGA); Fourier transform infrared spectroscopy (FTIR); and field emission scanning electron microscopy (FESEM)] in the curing time range of 3¿90 days at 25°C. Results from these tests showed that the best BFS/SCSA and H2O=Na2O ratios were 70=30 and 18.5, respectively. This study revealed an interesting valorization of the SCSA as a complementary precursor in BFS-based AABs because of the improvement of mechanical properties and the reduction in the consumption of BFS in AAB