Facile preparation of electrodes based on WO3 nanostructures modified with C and S used as anode materials for Li-ion batteries

Abstract

[EN] An appropriate morphological and structure matrix configuration where lithium ions could insert and de-insert is essential for lithium-ion batteries (LiB). Tungsten oxides (WO3) are especially attractive materials for this aim. In this research, the effects of the morphology and composition of WO3 nanostructures on the charge/discharge behavior for Li-ion batteries are methodically examined. On the one hand, nanostructured WO3 thin film was effectively synthesized by an electrochemical procedure. Then, an annealing treatment at 600°C in air environment for 4 h was carried out. In the second electrode synthesized, a carbon layer was uniformly deposited on WO3 nanostructures to obtain a WO3/C electrode. Finally, WO3/WS2 electrodes were prepared by means of in situ sulfurization of WO3 one-step solid-state synthesis using tungsten trioxide (WO3) and thiourea as precursor material. By using X-ray photoelectron spectroscopy, X-ray diffraction analysis, transmission electron microscopy, Raman spectra, and field-emission scanning electron microscopy, the three electrodes have been morphologically characterized. Electrochemical properties were analyzed by cyclic voltammogram, galvanostatic charge/discharge cycling, and electrochemical impedance spectroscopy. Among all the synthesized samples, WO3/C nanostructures reveal the best performance as they exhibit the greatest discharge capacity and cycle performance (820 mA h g¿1).