Comportamiento de membranas porosas de poliuretanos basados en policaprolactona y polietilenglicol para aplicaciones biomédicas

Abstract

[EN] Amphiphilic polyurethanes were synthesized from higth molecular eigth PEG and PCL diols as polymer segments and hexamethylene diisocyanate (HMDI) as binding agent. From these materials, biodegradable membranes were manufactured by freeze extraction using dioxane as solvent. Membranes having a microporous structure were obtained. Mechanical properties and hydrophilicity depended PEG content and porosity. Hydrolytic degradation was evaluated in a buffered saline. PCL / PEG=90/10 membranes maintained good mechanical properties and admit the lower water content after eight months of degradation. degradation rate showed higher relative to pure PCL membranes.

[ES] Poliuretanos amfifilicos fueron sintetizados a partir de dioles de PCL y PEG, de alto peso molecular, como segmentos poliméricos, y Hexametilendiisocianato (HMDI) como agente enlazante. A partir de estos materiales, se fabricaron membranas biodegradables mediante freeze extraction, usando dioxano como disolvente. Se obtuvieron membranas con una estructura microporosa. Las propiedades mecánicas y la hidrofilicidad dependían del contenido de PEG y la porosidad. Posteriormente se evaluó la degradación hidrolítica en un tampón salino. Las membranas PCL/PEG=90/10 mantenían buenas propiedades mecánicas y admitían el menor contenido de agua después de 8 meses de degradación y mostraban mayor velocidad de degradación respecto a las membranas de PCL pura.